说明:
低合金钢焊丝,与烧结型焊剂SJ102配合,可焊接600~700N/mm2抗拉强度等级的母材。
焊丝化学成分(%)
C | Mn | Si | S | P | |
保证值 | 0.06~0.11 | 1.60~1.90 | ≤0.25 | ≤0.030 | ≤0.030 |
例值 | 0.086 | 1.62 | 0.15 | 0.005 | 0.011 |
Ti | Cr | Ni | Cu | Mo | |
保证值 | ≤0.15 | ≤0.20 | ≤0.30 | ≤0.35 | 0.50~0.70 |
例值 | 0.11 | 0.074 | 0.055 | 0.19 | 0.55 |
熔敷金属力学性能
Rm (N/mm2) | ReL/Rp0.2(N/mm2) | A (%) | KV2 (J) -40℃ | |
SJ101 | 620~760 | ≥540 | ≥17 | ≥27 |
焊丝规格
焊丝直径(mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |